PlasmaChem nanomaterials

Bulk density: 0,69 g/cm3
Average cluster size: ca. 4 nm
Specific surface (BET): min. 350 m2/g
Non-diamond carbon content: traces
Controlled admixtures, %: Fe < 0,3; Cu < 0,01;
Zn < 0,01; Mn < 0,01; Si+Cr+Ca+Ti < 0,01
Losses at tempering: max. 2,4%
Ash content: <1,4%; Picnometric density: 3,18 g/cm3
Zeta potential: -50 ± 5 mV

Aqueous suspension of modified G01 nanodiamonds at 100mg/mL concentration.
Nanodiamonds with the surface modified by polyelectrolyte electrostatic adsorption.
Zeta potential: +50 ± 5 mV

Ash content: < 0,1%

Average diamond primary particle size: 4 nm
Diamond content: min. 20%
Ash content: < 6%

Most native 4 wt.% aqueous suspension of nanodiamonds, type PL-D-G01. The nanodiamonds are preserved in the most dispersed form.

Forms transparent stable colloidal solution of nanodiamonds in water and many polar
organic solvents. Free of additives and milling impurities.
Produced by chemical desintegration. Aqueous 5% solution.
Diamond crystallite size: 3,5-5,2 nm
Specific surface: 320-350 m2/g
Particle size (DLS): 5-15 nm
Ash content: <0,4%

Average diamond primary particle size: 4 nm
Diamond content: min. 20%
Ash content: < 0,3%